高冲击PA66 CM1011G45高模敷PA66 高冲击PA66 CM1011G45高模敷PA66 高冲击PA66 CM1011G45高模敷PA66
![]()
![]()
![]()
![]()
![]()
![]()
CM1011G-45 物性表
| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|
| 吸水率 (23℃.24小时) | 无水|1.9%水0.9|- | % | ASTM D-570 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|
| 泰伯磨耗量 ((1000g,CS-17)23℃) | 无水|1.9%水30|- | mg/1000次 | ASTM D-1044 |
| 比重 | 无水|1.9%水1.5|- |
| ASTM D-792 |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|
| 抗拉屈服强度 (23℃) | 无水|1.9%水2000|1300 | Kg/cm | ASTM D-638 |
| 挠曲模量 (23℃) | 无水|1.9%水122000|72000 | Kg/cm | ASTM D-790 |
| 抗剪强度 (23℃) | 无水|1.9%水940|750 | Kg/cm | ASTM D-732 |
| 挠曲模量 (80℃) | 无水|1.9%水63000|45000 | Kg/cm | ASTM D-790 |
| 断裂伸长率 |
|
| ASTM D-638 |
| (80℃) | 无水|1.9%水8|- | % |
|
| (23℃) | 无水|1.9%水5|5 | % |
|
| IZOD冲击强度 |
|
|
|
| (-40℃.无缺口1/8) | 无水|1.9%水92|95 | kg·cm/cm |
|
| (-40℃.无缺口1/2) | 无水|1.9%水12.5|15 | kg·cm/cm | ASTM D-256 |
| 压缩强度 (23℃) | 无水|1.9%水1900|- | Kg/cm | ASTM D-695 |
| 洛氏硬度 (23℃) | 无水|1.9%水95|- | M-标度 | ASTM D-785 |
| 挠曲强度 |
|
| ASTM D-790 |
| (23℃) | 无水|1.9%水2900|1850 | Kg/cm |
|
| (80℃) | 无水|1.9%水1600|- | Kg/cm |
|
| IZOD冲击强度 (23℃.V-缺口1/2) | 无水|1.9%水15|20 | kg·cm/cm | ASTM D-256 |
| 挠曲模量 (-40℃) | 无水|1.9%水140000|120000 | Kg/cm | ASTM D-790 |
| 断裂伸长率 (-40℃) | 无水|1.9%水4.5|- | % | ASTM D-638 |
| 压缩强度 (-40℃) | 无水|1.9%水|无水|1.9%水2600|-|2600|- | Kg/cm | ASTM D-695 |
| 洛氏硬度 (23℃) | 无水|1.9%水121|- | R-标度 | ASTM D-785 |
| 抗拉屈服强度 (-40℃) | 无水|1.9%水2900|- | Kg/cm | ASTM D-638 |
| 压缩强度 (80℃) | 无水|1.9%水|无水|1.9%水1000|-|1000|- | Kg/cm | ASTM D-695 |
| IZOD冲击强度 (23℃.无缺口1/8) | 无水|1.9%水98|120 | kg·cm/cm |
|
| 抗拉屈服强度 (80℃) | 无水|1.9%水1200|- | Kg/cm | ASTM D-638 |
| 挠曲强度 (-40℃) | 无水|1.9%水3300|- | Kg/cm | ASTM D-790 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|
| 损耗因数 (10Hz) | 无水|1.9%水0.02|0.06 |
| ASTM D-150 |
| 介电常数 (10Hz) | 无水|1.9%水4.2|4.5 |
| ASTM D-150 |
| 抗电弧性 (1/8") | 无水|1.9%水104|119 | s | ASTM D-495 |
| 介电强度 (1/8") | 无水|1.9%水19|15 | KV/mm | ASTM D-149 |
| 介电常数 (10Hz) | 无水|1.9%水4.9|7.4 |
| ASTM D-150 |
| 损耗因数 |
|
| ASTM D-150 |
| (10Hz) | 无水|1.9%水0.03|0.15 |
|
|
| (50Hz) | 无水|1.9%水|无水|1.9%水0.03|0.16|0.03|- |
|
|
| 体积电阻率 | 无水|1.9%水10|10 | Ω.cm | ASTM D-257 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|
| 熔点 | 无水|1.9%水225|- | ℃ | 差示扫描测热计DSC |
| 热挠曲温度 (4.6kg/cm) | 无水|1.9%水225|- | ℃ | ASTM D-648 |
| UL-94抗燃级 (1/16") | 无水|1.9%水HB|- |
| UL 94 |
| 线性热膨胀系数 | 无水|1.9%水2-3|- | ×10-5cm/cm/℃ | ASTM D-696 |
| 热挠曲温度 (18.6kg/cm) | 无水|1.9%水215|- | ℃ | ASTM D-648 |
| 比热 | 无水|1.9%水0.31|- | Cal/g·℃ |
|
| 其它性能 | 额定值 | 单位 | 测试方法 |
|---|
| 强化含量 | 无水|1.9%水45|- | WT% |
|
高冲击PA66,CM1011G45,高模敷PA66